Plastic Metal F - 500gm Kit

SKU: SWM000530B01V0002
MPN: 10150005
Availability: Available for Fast Dispatch.
Container Size


All Bulk Prices Below Are Quoted Including GST.
Buy 2 or above and pay only $77.89 each
  • Pasty form of epoxy plastic steel.
  • Aluminium filled and especially suitable for application to aluminium, aluminium alloys, magnesium and other light metals.
  • Non-corrosive and anti-magnetic.
  • Ideal for cost effective repair work and mould making.

Our Weicon Plastic Metal F is a high-quality grade of epoxy. This two-part compound is made from epoxy resin with aluminium filler and, once mixed, has a pasty consistency.

Plastic Metal F is typically used for repairs or coating on aluminium or other types of light metal. It is also used in mould making and repairs.

Once cured, it will have a glossy, aluminium grey appearance and set hard. Tensile strength is measured at 38 MPa and it will have a shore hardness of 80 Shore D.

Plastic Metal F has a fairly long pot life of around 60 minutes for a 500gm batch which will give you a good amount of time to apply. It will cure to 50% of its final strength after about 10 hours and be fully cured after about 24 hours (depending on environmental conditions).

This grade of plastic steel is completely non-corrosive and safe to use with aluminium, stainless and other kinds of metal. This epoxy compound is anti-magnetic and exhibits excellent electrical insulation properties.

Plastic metal F can be applied in layers up to 10mm in depth. After 7 hours of curing (per layer), additional layers can be applied if needed.

Easy to Use.

Weicon Plastic Metal F is a two-part epoxy. It has a mix ratio of 100:20 (resin / hardener). If using the whole kit at once though, there is no need for complex measuring as extra space has been left in the resin container for you to add the hardener and stir.

Far more information on how to use and apply this epoxy for best results is included on the Plastic Metal F TDS.

Basis Aluminium Filled Epoxy Resin
Mix Ratio (by Weight) 100 : 20 (Resin / Hardener)
Density of the Mixture 1.7 g/cm³
Viscosity of the Mixture 880,000 mPa·s
Colour Aluminium, Glossy
Maximum Layer Thickness 10mm
Mechanical Strength (80% of Final) 10 Hours (when curing at 20°C)
Final Strength 24 Hours (when curing at 20°C)
Mean Compressive Strength 61 MPa (DIN EN ISO 604)
Mean Tensile Strength 38 MPa (DIN EN ISO 527-2)
Bending Strength 37 MPa (DIN EN ISO 178)
e-Modulus (Tensile) 6,400 - 6,600 MPa (DIN EN ISO 527-2)
Shore Hardness 80 Shore D (DIN ISO 7619)
Continuous Temperature Rating -35°C to +120°C
Thermal Conductivity 1.4 W/m·K (DIN EN ISO 22007-4)
IMPA Reference Numbers 812921 (500gm) / 812922 (2kg)
ISSA Reference Numbers 75.509.09 (500gm) / 75.509.10 (2kg)
SKU SWM000530B01
Brand Weicon