Plastic Metal Ceramic BL Wear Resistant Epoxy - 500gm Kit

SKU: SWM000245B01V0002
MPN: 10400005
Availability: Available for Fast Dispatch.
Container Size


All Bulk Prices Below Are Quoted Including GST.
Buy 2 or above and pay only $152.65 each
  • Extremely wear resistant epoxy coating for metals and other high abrasion surfaces.
  • Liquid, brushable and self-levelling.
  • High heat resistance (180°C) and very good chemical resistance.

Manufactured by Weicon in Germany, our Plastic Metal Ceramic BL is a specialised epoxy coating that is used to line, coat and protect stressed surfaces. Ceramic BL is blue in colour and has a liquid consistency that allows it to be brushed onto surfaces (or sprayed).

Ceramic BL epoxy coating has excellent wear resistance and effectively protects coated surfaces from abrasion across a long service life.

Ceramic BL is made from a specialised type of epoxy resin that is filled with silicon carbide and zirconium silicate. It is a two-part epoxy that must be mixed before use. Once it’s mixed, you have a working pot life of about 40 minutes (assuming 20°C and 200gm mixed).

You can create coatings up to 10mm thick in a single pour with Ceramic BL. After 16 hours the epoxy will be capable of bearing mechanical loads while full cure will take about 24 hours.

Applications for Plastic Metal Ceramic BL

Weicon Ceramic BL Plastic Metal is widely used in numerous industries around the world to protect stressed metal and other surfaces from abrasion. Specific application examples include:

  • The lining of heavily stressed pump housings.
  • Wear protection for slide bearings.
  • Abrasion protection on slides and funnels.
  • The lining and pipes and flanges.
  • Repair of castings, valves and blower fans.
  • For the repair of metal components and the lining of stressed parts in the marine industry (IMPA and ISSA Registered).
  • For lining trays and bins in the mining sector.
  • In apparatus engineering and construction.
Basis Mineral Filled Epoxy Resin
Mix Ratio 100 : 15 (Resin / Hardener)
Density of the Mixture 1.8 g/cm³
Viscosity of the Mixture 6,000 MPa
Colour Blue
Maximum Layer Thickness 10mm
Mechanical Strength (50% of Final) 16 Hours (when curing at 20°C)
Final Strength 24 Hours (when curing at 20°C)
Pressure 85 MPa (at 25°C, DIN 53281-83)
Bending Strength 95 MPa (at 25°C, DIN 53281-83)
Mean e-Modul 7,000 - 8,000 MPa (at 25°C, DIN 53281-83)
Shore Hardness 83 Shore D ( (at 25°C, DIN 53281-83)
Shrinkage During Cure 0.02%
Thermoforming Resistance +80°C
Continuous Temperature Rating -35°C to +180°C
Thermal Conductivity 0.7 W/m·K (ISO 8894-2)
Dielectric Strength  15 kV/mm
IMPA Reference Number 75.509.19 (500gm) / 75.509.20 (2kg)
ISSA Reference Number 81 29 37 (500gm) / 81 29 38 (2kg)
SKU SWM000245B01
Brand Weicon